| Item | Index | |
|---|---|---|
| Appearance | Colorless, odorless, tasteless and lustrous transparent solid. | |
| Purity %≥ | 98 | |
| Melting point ℃ | 212 °C | |
| Resins | Polymer Matrix Structure | Physical Form Appearance | Particle Size | Specific Gravity | Shipping Weight in H | Wear Ability | Leachable |
|---|---|---|---|---|---|---|---|
| DL-1 | Polypropylene | White Spherical Beads | 02.5-4.0mm | 0.9-0.95 mg/ml | 300-350 g/L | 98% | 3% |
| DL-2 | Polypropylene | White Spherical Beads | Φ1.3±0.1mmL1.4±0.1mm | 0.88-0.92 mg/ml | 500-570 g/L | 98% | 3% |
| STR | Polypropylene | White Spherical Beads | 0.7-0.9mm | 1.14-1.16 mg/ml | 620-720 g/L | 98% | 3% |
| Packing | in 25kg bags |
|---|---|
| Storage | 20°C,2 years |
| Shipping | Room temperature in China;may vary elsewhere |
Tel: 0086 25 52397805
Email: info@nj-finechem.com
| Common Names | Wang resin | ||
|---|---|---|---|
| Structure |  |
||
| CAS No. | 201058-08-4 | Boiling Point (℃) | 386.2ºC at 760 mmHg |
| Molecular Weight | 228.286 | Melting Point (℃) | N/A |
| Appearance | Off-white to beige beads | Vapor Specific Gravity | - |
| HS Code | 3909400000 | Flash Point (℃) | 175.2ºC |
| Solubility | - | Autoignition Temperature (℃) | - |
| Safety Phrases | 26-36/37/39-24/25 | ||
|---|---|---|---|
| RIDADR | 2211 | ||
| WGK Germany | 3 | ||
| Packaging Group | III | ||
| Hazard Class | - | ||
| SYMPTOMS | PREVENTION | FIRST AID | |
| Inhalation | poisonous | wear a mask | fresh air,keep breath comfortable |
| Skin | skin burn | wear protective clothing | Remove all soiled clothing and wash your skin with water. |
| Eyes | eye injury | wear goggles | Rinse slowly and gently with water for a few minutes |
| Ingestion | poisonous | Do not eat, drink or smoke while using this product | Call a POISON CENTRE or doctor |
What is Inert And Polymer Beads?
Inert And Polymer Beads are used to create a barrier in an ion exchange bed and keep the ion exchange beads exactly where they are supposed to be. They can guard the bottom collectors, the top distributors and create separation between cation and anion layers in a mixed bed.
How is Inert And Polymer Beads stored and distributed?
1. Handling, loading and unloading operations should be gentle, stable and regular, do not hit hard.
If the ground is wet and slippery, pay attention to prevent slipping.
2. The storage temperature of this material should not be higher than 90 ℃, and the service
temperature should be 180 ℃.
3. The storage temperature is above 0 ℃ in wet state. Please keep the package well sealed in case of
water loss during storage; In case of dehydration, the dry resin should be soaked in ethanol for
about 2 hours, cleaned with clean water, and then repackaged or used.
4. Prevent the ball from freezing and cracking in winter. If freezing is found, melt slowly at room
temperature.
5. In the process of transportation or storage, it is strictly forbidden to stack with odors, toxic
substances and strong oxidants.
What is Inert And Polymer Beads used for?
Inert resin is mainly used for water treatment with high salt content; Large amount of water softening and dealkali treatment; Neutralization of waste acid and alkali; Treatment of electroplating wastewater containing copper and nickel; It can also be used for the recovery and treatment of waste liquid, the separation and purification of biochemical drugs.
1. It plays the role of regenerant distribution during regeneration.
2. During operation, it can intercept the fine resin to avoid blocking the outlet hole or the gap of the filter cap.
3. Adjust the resin filling rate. The quality of floating bed is related to resin filling rate. The filling rate is too small to form a bed; If the filling rate is too high, the resin will be filled up after transformation and expansion, and the white ball can play a small role in regulating.